NOVA Chemicals Dylark® 378P15 Glass Reinforced Engineering Resin

Category Polymer , Thermoplastic , SMA Polymer , Glass Reinforced, Modified SMA
Manufacturer NOVA Chemicals
Trade Name Dylark®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF NOVA Chemicals Dylark® 378P15 Glass Reinforced Engineering Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Very high modulus, High heat resistance, excellent flow characteristics, excellent adhesion to urethaneApplications: Instrument panel substrates, Consoles, Cluster housings, Interior trim
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ISO 1183
Filler Content 15 %
15 %
Glass Fiber; ISO 3451-1
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm
0.0030 - 0.0050 in/in
ISO 2577
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 64.0 MPa
9280 psi
ISO 527-2
Elongation at Yield 2.2 %
2.2 %
ISO 527-2
Tensile Modulus 5.30 GPa
769 ksi
ISO 527-2
Flexural Strength 100 MPa
14500 psi
ISO 178
Flexural Modulus 4.50 GPa
653 ksi
ISO 178
Izod Impact, Notched (ISO) 8.20 kJ/m²

@Temperature -40.0 °C
3.90 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
8.50 kJ/m²

@Temperature 23.0 °C
4.04 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 2.16 J/cm²
10.3 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.840 J/cm²
4.00 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 55.8 µm/m-°C
31.0 µin/in-°F
NOVA Chemicals Laboratory Procedure
Deflection Temperature at 1.8 MPa (264 psi) 122 °C

@Thickness 4.00 mm
252 °F

@Thickness 0.157 in
Unannealed; ISO 75-2
Processing Properties Metric English Comments
Processing Temperature 249 - 288 °C
480 - 550 °F
Profile temperatures
Melt Temperature 260 - 288 °C
500 - 550 °F
Air purge at equilibrium conditions
Mold Temperature 43.3 - 60.0 °C
110 - 140 °F
Core mold surface temperature at equilibrium conditions
54.4 - 71.1 °C
130 - 160 °F
Cavity mold surface temperature at equilibrium conditions
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Screw Speed 80 - 125 rpm
80 - 125 rpm
Descriptive Properties Value Comments
Injection Speed medium-fast