Multibase SILASTIC® Q7-4720 Dow-Corning Biomedical Grade ETR Elastomer

Category Polymer , Thermoset , Silicone
Manufacturer Multibase
Trade Name SILASTIC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase SILASTIC® Q7-4720 Dow-Corning Biomedical Grade ETR Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
as molded- 10 minutes at 116°C
Mechanical Properties Metric English Comments
Hardness, Shore A 22
22
as molded- 10 minutes at 116°C
46
46
post cured- 2 hours at 177°C
46
46
post cured- 4 hours at 177°C
46
46
post cured- 8 hours at 177°C
Tensile Strength, Ultimate 9.108 MPa
1321 psi
post cured- 8 hours at 177°C
9.287 MPa
1347 psi
as molded- 10 minutes at 116°C
9.646 MPa
1399 psi
post cured- 4 hours at 177°C
9.784 MPa
1419 psi
post cured- 2 hours at 177°C
Tensile Strength, Yield 0.400 MPa
58.0 psi
at 200%, as molded- 10 minutes at 116°C
1.43 MPa
207 psi
200%, post cured- 4 hours at 177°C
1.48 MPa
215 psi
200%, post cured- 8 hours at 177°C
1.53 MPa
222 psi
at 200%, post cured- 2 hours at 177°C
Elongation at Break 742 %
742 %
post cured- 8 hours at 177°C
767 %
767 %
post cured- 2 hours at 177°C
771 %
771 %
post cured- 4 hours at 177°C
1283 %
1283 %
as molded- 10 minutes at 116°C
Tear Strength 29.5 kN/m
168 pli
post cured- 4 hours at 177°C; Die B
30.7 kN/m
175 pli
post cured- 2 hours at 177°C; Die B
32.3 kN/m
184 pli
as molded- 10 minutes at 116°C; Die B
33.8 kN/m
193 pli
post cured- 8 hours at 177°C; Die B
Compression Set 25.6 %
25.6 %
22 hours at 177°C, post cured- 8 hours at 177°C
30.1 %
30.1 %
22 hours at 177°C, as molded-10 minutes at 116°C
33.6 %
33.6 %
22 hours at 177°C, post cured- 2 hours at 177°C
41.1 %
41.1 %
22 hours at 177°C, post cured- 4 hours at 177°C