- Multibase Multi-Pro® 4810 C White 47.7% Filler Content Polypropylene
Multibase Multi-Pro® 4810 C White 47.7% Filler Content Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 4810 C White 47.7% Filler Content Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Moisture content is 0.04%. Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Melt Flow | 15.2 g/10 min | 15.2 g/10 min | (Condition L) ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 12.8 MPa | 1860 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Strength | 22.5 MPa | 3260 psi | ASTM D790-92 |
| Flexural Modulus | 1.579 GPa | 229.0 ksi | Method 1, Proc. B; ASTM D-790 |
| Izod Impact, Notched | 2.56 J/cm | 4.80 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 15.4 J | 11.4 ft-lb | ASTM D5420-93 |
Users viewing this material also viewed the following:
- Nye Lubricants 734B (RL) Synthetic Oil
- SABIC Innovative Plastics Lexan® OQ4120R PC
- Resinoid 1340 Phenolic Molding, Glass Reinforced
- LNP Thermocomp® LF-1004 Polyetheretherketone, Glass Fiber Reinforcement (discontinued **)
- Fiberfil® PP-60/TC/15/VO/ND Polypropylene Homopolymer, 15% Talc Filled, Flame Retardant
- Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F)
- PlastxWorld Veroplas PB2001F Nylon 66
- China Tungsten WC 96 Tungsten Carbide Powder
- Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved