Multibase Multi-Pro® 0505 RC Black 5.2% Glass Filled Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 0505 RC Black 5.2% Glass Filled Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This product was specially designed for one customer's glass filled polypropylene application.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.948 g/cc | 0.0342 lb/in³ | ASTM D792-91 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955-89 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM D638-95 |
| Elongation at Break | 34 % | 34 % | ASTM D638-95 |
| Flexural Strength | 50.3 MPa | 7300 psi | ASTM D790-95 |
| Flexural Modulus | 1.661 GPa | 240.9 ksi | Method 1, Proc. B; ASTM D-790-95 |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256-93a |
| Gardner Impact | 3.40 J | 2.51 ft-lb | ASTM D5420-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 65.0 °C | 149 °F | ASTM D648-95 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | ASTM D648-95 |
Users viewing this material also viewed the following:
- Radici Heraflex® E 5620 TPC-ET Thermoplastic Elastomer
- Ravago Manufacturing Americas Hylon® N2040MGHL Nylon 6 (DAM)
- SABIC R50035 Linear Low Density Polyethylene for Rotational Molding
- Isoflon Tisoflon® 6K Polytetrafluoroethylene Coated Kevlar Fabric
- UBE UBESTA® 3030U Nylon 12 (After Ethanol for 500 hours)
- Tra-Con Tra-Bond F230 Color Keyed High Temperature Epoxy Adhesive
- E-Polymers TEKANATE® G7010FR General Purpose Flame Retardant Polycarbonate
- C.O.I.M. LARIPUR® LPR5925 Special Adipate Ester Polyurethane
- ArcelorMittal Dual Phase 600 Very high strength steel, Hot Rolled Steel
Copyright © lookpolymers.com All Rights Reserved