Multibase Multi-Flex® TPO D 3218
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® TPO |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TPO D 3218.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Multi-Flex® TPO D 3218 is a compound for automotive applications replacing Himont's 7023. The burn rate is 0.6 in/min; ASTM FM VSS 30.Data provided by Multibase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792-91 |
| Melt Flow | 18 g/10 min | 18 g/10 min | (Condition L) ASTM D-1238-94a |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 32 | 32 | 10 sec; ASTM D-2240-95 |
| Tensile Strength, Ultimate | 5.10 MPa | 740 psi | ASTM D638-95 |
| Elongation at Break | 450 % | 450 % | ASTM D638-95 |
| Flexural Strength | 4.10 MPa | 595 psi | ASTM D955-89 |
| Flexural Modulus | 0.1448 GPa | 21.00 ksi | Method 1, Proc. B; ASTM D-790-95 |
Users viewing this material also viewed the following:
- Pyrotek AL-THERM 2100H Vacuum formed refractories for use with modular hot top systems
- SABIC Innovative Plastics Lexan® 141R PC
- MetalTek C18100 Chrome Zirc Copper High Conductivity
- ExxonMobil Univis HVI 13
- ChevronTexaco Multifak® EP NLGI Grade 2
- Eurostar Staramide BG8 PA6, 40% Glass Fiber Filled, Injection Molded
- Arkema Group OREVAC® 18302N Maleic Anhydride Modified Linear Low Density Polyethylene
- Adamas Adalon® 812 PTFE, 46% Bronze, Green
- SABIC Innovative Plastics PC2200 PC
- Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C
Copyright © lookpolymers.com All Rights Reserved