- Multibase Multi-Flex® TEA 4001-35 Natural TPO Thermoplastic Polyolefin Elastomer
Multibase Multi-Flex® TEA 4001-35 Natural TPO Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® TEA 4001-35 Natural TPO Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.942 g/cc | 0.942 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | ASTM D955 |
| Melt Flow | 75 g/10 min @Load 2.16 kg, Temperature 230 °C |
75 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 40 | 40 | 10 seconds; ASTM D2240 |
| 45 | 45 | ASTM D2240 | |
| Tensile Strength, Yield | 6.41 MPa | 930 psi | Elastic; ASTM D412 |
| Elongation at Break | 920 % | 920 % | Elastic; ASTM D412 |
| Tear Strength | 26.3 kN/m | 150 pli | ASTM D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 193 °C | 380 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 210 °C | 410 °F | |
| Mold Temperature | 35.0 °C | 95.0 °F |
Users viewing this material also viewed the following:
- Overview of materials for High Density Polyethylene (HDPE), Blow Molding Grade
- Karina 858-12/20-IS-RG PVC Compound
- Mitsubishi Xantar® FC 19 UR Polycarbonate
- Solvay TECHNYL® A 218W V15 PA66, 15% glass fiber, DRY
- Borealis HE365FB Polypropylene
- Dow CYCLOTENE™ 4024-40 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- 3M Dyneon™ CC103 Custom Fluoropolymer Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved