Multibase Multi-Flex® D 3604 TPE Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Multibase |
| Trade Name | Multi-Flex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Flex® D 3604 TPE Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Chemical Resistance, Good Colorability, GoodElasticity, HighElectrically InsulatingFlame RetardantFlexibility, GoodHeat StabilizedOzone ResistantProcessability, GoodUV Resistance, Good PaintableForms:PelletsProcessing Method:Injection Molding Information provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | 10 seconds; ASTM D2240 |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ASTM D638 |
| Elongation at Break | 680 % | 680 % | ASTM D638 |
| Flexural Modulus | 0.128 GPa | 18.5 ksi | 1% Secant; ASTM D790 |
| Tear Strength | 50.8 kN/m | 290 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | -50.0 °C | -58.0 °F | ASTM D746 |
| Flame Spread | 18 mm/min | 0.71 in/min | FM VSS-302 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 °C | 410 °F | |
| Front Barrel Temperature | 227 °C | 440 °F | |
| Nozzle Temperature | 235 °C | 455 °F | |
| Mold Temperature | 51.7 °C | 125 °F | |
| Drying Temperature | 51.7 °C | 125 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 3.45 - 4.83 MPa | 500 - 700 psi | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Screw Speed | 40 rpm | 40 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamp Tonnage | 1.5-2.5 tons/in2 | |
| Fogging | Min. 90 | SAE-J275 |
| Injection Rate | Fast | |
| Suggested Max Regrind | 0.5 |