Multibase C6-350 LH Parts A and B Dow-Corning Class VI Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Multibase
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Multibase C6-350 LH Parts A and B Dow-Corning Class VI Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Multibase
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
Relative; ASTM D792V
Mechanical Properties Metric English Comments
Hardness, Shore A 49
49
no post cure; ASTM D2240
56
56
post cured- 2 hours at 177°C; ASTM D2240
56
56
post cured- 4 hours at 177°C; ASTM D2240
57
57
post cured- 8 hours at 177°C; ASTM D2240
Tensile Strength, Ultimate 7.79 MPa
1130 psi
post cured- 8 hours at 177°C; ASTM D412
7.963 MPa
1155 psi
post cured- 2 hours at 177°C; ASTM D412
8.081 MPa
1172 psi
post cured- 4 hours at 177°C; ASTM D412
8.536 MPa
1238 psi
no post cure; ASTM D412
Tensile Strength, Yield 2.21 MPa
321 psi
at 200%, no post cure; ASTM D412
3.39 MPa
491 psi
200%, post cured- 4 hours at 177°C; ASTM D412
3.49 MPa
506 psi
at 200%, post cured- 2 hours at 177°C; ASTM D412
3.61 MPa
524 psi
200%, post cured- 8 hours at 177°C; ASTM D412
Elongation at Break 473 %
473 %
post cured- 8 hours at 177°C; ASTM D412
510 %
510 %
post cured- 4 hours at 177°C; ASTM D412
511 %
511 %
post cured- 2 hours at 177°C; ASTM D412
732 %
732 %
no post cure; ASTM D412
Tear Strength 37.9 kN/m
216 pli
Die B, no post cure; ASTM D624
42.4 kN/m
242 pli
Die B, post cured- 8 hours at 177°C; ASTM D624
43.3 kN/m
247 pli
Die B,post cured- 2 hours at 177°C; ASTM D624
45.2 kN/m
258 pli
Die B, post cured- 4 hours at 177°C; ASTM D624
Compression Set 60 %
60 %
no post cure; ASTM D395
Thermal Properties Metric English Comments
Shrinkage 1.7 %
1.7 %
no post cure