Momentive Performance Materials Silmate® RTV1473 Black, One Component, Silicone Rubber

Category Polymer , Adhesive , Thermoset , Silicone , Silicone, RTV, Adhesive/Sealant Grade
Manufacturer Momentive Performance Materials (Former GE Silicones)
Trade Name Silmate®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Momentive Performance Materials Silmate® RTV1473 Black, One Component, Silicone Rubber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Silmate RTV1473 silicone rubber is a black, on-component, ready-to-use sealant designed for formed-in-place gasketing applications where good oil resistance is a design consideration. RTV1473 silicone rubber has a paste-like consistency when initially dispensed and cures on exposure to atmospheric moisture at room temperature to form an elastomeric, resilient silicone rubber gasket.The paste consistency of RTV1473 silicone rubber allows the product to flow only with external pressure. As a result RTV1473 silicone rubber can be applied to horizontal, vertical, or overhead surfaces in thicknesses up to 6mm(1/4in.).RTV1473 silicone rubber utilizes a moisture vapor cure system which release acetic acid vapors from the sealant surface as a by-product of cure.RTV 1473 silicone rubber exhibits flow characteristics for rapid dispensing with standard pumping equipment used in assembly line production systems.Key Performance Properties: One component productThixotropic paste consistencyCapability to cure at room temperature and ambient humidity conditionsPrimerless adhesion to many substratesRetains elastomeric properties for long periods at temperatures up to 204°C(400°F) and for short periods up to 260°C(500°F)Low temperature flexibilityHigh quality weatherability and ozone and oil resistanceConforms to surface voids and irregularities to form a positive seal in mated surfacesFlow characteristics allow rapid dispensing with automated equipmentApplications: Two types of formed-in-place gasketing applications can be selected: a wet bead method and a cured bead method.The wet bead method involves mating parts before RT1473 silicone rubber cure has been completed. This method provides the best seal but makes future disassembly more difficult.In applications where easy disassembly/reassembly of parts is desired, the cured bead method should be considered. This method involves dispensing the RTV1473 on one surface and allowing it to fully cure before mechanically joining the surfaces.RTV1473 silicone rubber is not for use in delicate electrical and electronic applications in which corrosion of copper, brass, or other sensitive metals is undesirable. Not for use in contact with gasoline.GE Silicones became a part of Momentive Performance Materials in 2006.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 30
30
Tensile Strength, Ultimate 3.09 MPa
448 psi
Elongation at Break 500 %
500 %
Shear Strength 1.373 MPa
199.1 psi
Tear Strength 7.85 kN/m
44.8 pli
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
399 °F
Continuous
Brittleness Temperature -60.0 °C
-76.0 °F
Processing Properties Metric English Comments
Cure Time 25.0 min

@Temperature 25.0 °C
0.417 hour

@Temperature 77.0 °F
Tack-free, 50% R.H.
Descriptive Properties Value Comments
Application rate 380 g/min
Color Black
Consistency Soft Paste