Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsui AURUM® JGN3030 Polyimide, Glass Fiber Filled  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AURUM JGN3030 is a high performance thermoplastic polyimide for precision injection molded components and extruded products. A member of the AURUM family of advanced engineering resins, glass fiber reinforced AURUM JGN3030 offers a unique balance of mechanical and thermal properties for superior performance in demanding automotive, business machinery, industrial equipment, aerospace, and semiconductor equipment applications. AURUM exhibits outstanding resistance to chemicals and radiation, a low coefficient of thermal expansion, excellent electrical properties, and flame resistance.Applications: AURUM JGN3030 injection molded components are excellent replacements for metals, ceramics, and other plastics. High performance AURUM JGN3030 parts include heat-resistant gears, semiconductor manufacturing and handling equipment components, and thermal and electrical insulators.Information provided by DuPont
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D792
Water Absorption 0.23 %
0.23 %
24 hrs @ 73°F; ASTM D570
Moisture Absorption at Equilibrium 0.10 %
0.10 %
73°F; 60 RH, 24hrs
Linear Mold Shrinkage 0.0044 cm/cm
0.0044 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 165 MPa
23900 psi
ASTM D638
106 MPa

@Temperature 149 °C
15400 psi

@Temperature 300 °F
ASTM D638
Elongation at Yield 3.0 %
3.0 %
ASTM D638
4.0 %

@Temperature 149 °C
4.0 %

@Temperature 300 °F
ASTM D638
Flexural Strength 241 MPa
35000 psi
ASTM D790
172 MPa

@Temperature 149 °C
25000 psi

@Temperature 300 °F
ASTM D790
Flexural Modulus 9.65 GPa
1400 ksi
ASTM D790
8.27 GPa

@Temperature 149 °C
1200 ksi

@Temperature 300 °F
ASTM D790
Compressive Strength 88.3 MPa

@Temperature 149 °C
12800 psi

@Temperature 300 °F
JIS K7208
188 MPa

@Temperature 22.8 °C
27300 psi

@Temperature 73.0 °F
JIS K7208
Izod Impact, Notched 1.17 J/cm
2.20 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 16.2 µm/m-°C

@Temperature 22.8 °C
9.00 µin/in-°F

@Temperature 73.0 °F
MD; ASTM D696
52.2 µm/m-°C

@Temperature 73.0 °C
29.0 µin/in-°F

@Temperature 163 °F
TD; ASTM D696
Specific Heat Capacity 0.962 J/g-°C
0.230 BTU/lb-°F
DSC
0.9623 J/g-°C

@Temperature 100 °C
0.2300 BTU/lb-°F

@Temperature 212 °F
DSC
1.339 J/g-°C

@Temperature 300 °C
0.3200 BTU/lb-°F

@Temperature 572 °F
DSC
Thermal Conductivity 0.348667 W/m-K
2.41975 BTU-in/hr-ft²-°F
Melting Point 388 °C
730 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 245 °C
473 °F
ASTM D648
Glass Transition Temp, Tg 250 °C
482 °F
DSC
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
Electrical Properties Metric English Comments
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
ASTM D257
Dielectric Constant 3.7

@Frequency 1e+6 Hz
3.7

@Frequency 1e+6 Hz
ASTM D150
3.8

@Frequency 1000 Hz
3.8

@Frequency 1000 Hz
ASTM D150
Dissipation Factor 0.0012

@Frequency 1000 Hz
0.0012

@Frequency 1000 Hz
ASTM D150
0.0036

@Frequency 1e+6 Hz
0.0036

@Frequency 1e+6 Hz
ASTM D150