Mitsui APELâ„¢ APL8008T Cyclo Olefin Copolymer (COC)
| Category | Polymer , Thermoplastic , Cyclo Olefin Polymer |
| Manufacturer | Mitsui Chemicals America |
| Trade Name | APEL™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsui APELâ„¢ APL8008T Cyclo Olefin Copolymer (COC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This material possesses many characteristics inherent in polyolefins such as excellent electrical insulating properties and outstanding moisture resistance. In addition, it features good melt processability/flowability, good clarity and transparency, high glass transition temperature (Tg), exceptional moisture impermeability, impressive gas barrier qualities and excellent chemical and heat resistance. This material is used in Film Sheet applications.Information provided by Mitsui Chemicals America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Moisture Vapor Transmission | 0.0900 cc-mm/m²-24hr-atm | 0.229 cc-mil/100 in²-24hr-atm | 1 atm; ASTM D1249 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | MCI Method |
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 260 °C |
15 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 80.0 °C | 176 °F | TMA; MCI Method |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | MCI Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.54 | 1.54 | ASTM D542 |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |
Users viewing this material also viewed the following:
- MV Labs NH1000 (NH4)2SO4 Ammonium sulfate
- Polykemi AB POLYelast TPE S902A Thermoplastic Elastomer, SBS-based
- PlastiComp Complet® LGF50 - TPU Rigid Thermoplastic Polyurethane, 50% Long Glass Fiber Reinforced
- SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer (Asia Pacific)
- Kazanorgsintez NMPE-2 Low-Molecular Polyethylene
- Multibase C6-265 VAROX DBPH Dow-Corning Class VI Elastomer
- SABIC Innovative Plastics LNP LUBRICOMP KAL22 Acetal Copolymer (Europe-Africa-Middle East)
- AK Steel Hot Rolled Carbon Steel, Drawing Steel (DS Type B), Standard Grade
- ATI Allvac® Nickelvac® 600 Nickel Superalloy, Heat Treatment: 927°C (1700°F) Anneal
Copyright © lookpolymers.com All Rights Reserved