Mitsubishi Xantar® SF 2220 Polycarbonate-20% Glass Reinforced

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled
Manufacturer Mitsubishi
Trade Name Xantar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Xantar® SF 2220 Polycarbonate-20% Glass Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
Foamed; ISO 1183
1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
Sim. to ISO 62
Viscosity Test 48 cm³/g
48 cm³/g
Limiting Viscosity Number; ISO 1628-4
Melt Flow 8.1 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.1 g/10 min

@Load 2.65 lb,
Temperature 572 °F
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
ISO 527-1/-2
Elongation at Break 3.0 %
3.0 %
ISO 527-1/-2
Tensile Modulus 4.10 GPa
595 ksi
ISO 527-1/-2
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 4.30 GPa
624 ksi
ISO 178
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 12.0 µm/m-°C

@Temperature 20.0 °C
6.67 µin/in-°F

@Temperature 68.0 °F
ISO 11359-1/-2
Maximum Service Temperature, Air 125 °C
257 °F
Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
ISO 75-1/-2
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
5VA

@Thickness 4.80 mm
5VA

@Thickness 0.189 in
IEC 60695-11-20
Oxygen Index 35 %
35 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.3

@Frequency 100 Hz
3.3

@Frequency 100 Hz
IEC 60250
3.3

@Frequency 1e+6 Hz
3.3

@Frequency 1e+6 Hz
IEC 60250
Dissipation Factor 0.00080

@Frequency 100 Hz
0.00080

@Frequency 100 Hz
IEC 60250
0.0090

@Frequency 1e+6 Hz
0.0090

@Frequency 1e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Flame Retardant Yes
Flame Retarding Agent Yes
Injection molding Yes
With Fillers Yes