Mitsubishi Xantar® MX 1082 Polycarbonate-20% Glass Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Mitsubishi |
| Trade Name | Xantar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mitsubishi Xantar® MX 1082 Polycarbonate-20% Glass Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 0.29 % | 0.29 % | Sim. to ISO 62 |
| Viscosity Test | 56 cm³/g | 56 cm³/g | Limiting Viscosity Number; ISO 1628-4 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Melt Flow | 4.05 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.05 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 3 cm<sup>3</sup>/10min.; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 91 | 91 | ISO 2039-2 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1/-2 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1/-2 |
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/4A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
ISO 11359-1/-2 |
| Maximum Service Temperature, Air | 125 °C | 257 °F | Ball Pressure Temperature; IEC 60695-10-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ISO 75-1/-2 |
| Vicat Softening Point | 150 °C | 302 °F | 50°C/h 50N; ISO 306 |
| UL RTI, Electrical | 130 °C @Thickness 1.50 mm |
266 °F @Thickness 0.0591 in |
UL746B |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL746B | |
| UL RTI, Mechanical with Impact | 125 °C @Thickness 1.50 mm |
257 °F @Thickness 0.0591 in |
UL746B |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL746B | |
| UL RTI, Mechanical without Impact | 125 °C @Thickness 1.50 mm |
257 °F @Thickness 0.0591 in |
UL746B |
| 130 °C @Thickness 3.00 mm |
266 °F @Thickness 0.118 in |
UL746B | |
| Flammability, UL94 | V-0 @Thickness 1.20 mm |
V-0 @Thickness 0.0472 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
IEC 60695-11-10 | |
| Oxygen Index | 33 % | 33 % | ISO 4589-1/-2 |
| Glow Wire Test | 850 °C @Thickness 1.50 mm |
1560 °F @Thickness 0.0591 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 |
| 875 °C @Thickness 3.00 mm |
1610 °F @Thickness 0.118 in |
Glow Wire Ignition Temperature; IEC 60695-2-13 | |
| 960 °C @Thickness 1.50 mm |
1760 °F @Thickness 0.0591 in |
Glow Wire Flammability Index; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
Glow Wire Flammability Index; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
IEC 60250 |
| 3.25 @Frequency 100 Hz |
3.25 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.00090 @Frequency 100 Hz |
0.00090 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1e+6 Hz |
0.0090 @Frequency 1e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| 175 - 249 V | 175 - 249 V | PLC 3; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flame Retardant | Yes | |
| Flame Retarding Agent | Yes | |
| Injection molding | Yes | |
| Release Agent | Yes | |
| With Fillers | Yes |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8172R (829RP) (UF) Synthetic Oil
- Plaskolite West Optix® CP - 41 General Purpose Acrylic Resin
- Techmer ES HiFill® PA12 GF30 HS L 30% Glass Filled
- Samyang Trirex® PC-3025N2 10 MFI Flame Retardant Clear Polycarbonate
- Von Roll Isola IMI Varnish 708 Solventless Polyester Varnish for Electrical Insulation
- Colorite Polymers MULTICHEM™ 7514 Vinyl-Urethane Blend
- 3M Scotch-Weld™ 78 HT Hi-Temperature Polystyrene Foam Insulation Cylinder Spray Adhesive
- BASF Ultramid® A4H PA66 (Dry)
- Momentive Performance Materials HV 3/606 Heat Cured Rubber - High Temperature
- Chevron Phillips 7109DJT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved