Mitsubishi Xantar® C CE 407 Polycarbonate/ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Mitsubishi
Trade Name	Xantar®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsubishi Xantar® C CE 407 Polycarbonate/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The Xantar® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the Xantar® product line from DSM in 2010.

Physical Properties	Metric	English	Comments
Density	1.19 g/cc	0.0430 lb/in³	ISO 1183
Water Absorption	0.60 %	0.60 %	Sim. to ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Humidity Absorption; Sim. to ISO 62
Melt Flow	13.09 g/10 min @Load 5.00 kg, Temperature 260 °C	13.09 g/10 min @Load 11.0 lb, Temperature 500 °F	Calculated from Volume Flow Rate of 11 cm<sup>3</sup>/10min.; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	ISO 527-1/-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-1/-2
Tensile Modulus	2.70 GPa	392 ksi	ISO 527-1/-2
Izod Impact, Notched (ISO)	60.0 kJ/m² @Temperature -20.0 °C	28.6 ft-lb/in² @Temperature -4.00 °F	ISO 180/4A
	80.0 kJ/m² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	ISO 180/4A
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	110 °C	230 °F	Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	100 °C	212 °F	ISO 75-1/-2
Vicat Softening Point	120 °C	248 °F	50°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
Oxygen Index	32 %	32 %	ISO 4589-1/-2
Glow Wire Test	800 °C @Thickness 1.50 mm	1470 °F @Thickness 0.0591 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	800 °C @Thickness 1.50 mm	1470 °F @Thickness 0.0591 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	960 °C @Thickness 1.50 mm	1760 °F @Thickness 0.0591 in	Glow Wire Flammability Index; IEC 60695-2-12
	960 °C @Thickness 1.50 mm	1760 °F @Thickness 0.0591 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.0 @Frequency 1e+6 Hz	3.0 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112
	>= 600 V	>= 600 V	PLC 0; UL 746A

Descriptive Properties	Value	Comments
Flame Retardant	Yes
Flame Retarding Agent	Yes
Other Extrusion	Yes
Profile extrusion	Yes
Release Agent	Yes
Without Fillers	Yes