Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer Mitsubishi
Trade Name Hostaphan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Mitsubishi Hostaphan® RN, 30 micron Nominal Thickness Universal Polyethylene Terephthalate Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Hostaphan® RN is a transparent, biaxially oriented film made of polyethylene terephthalate (PET) and characterized by outstanding physical properties. Hostaphan® RN is the standard product for the following applications:Films for packagingCoatingLaminatingMetallizingPrintingDecorative filmsGloss laminationsAdhesive tapesInsulation tapesReleaseTransfer filmRelease film for thermosetting resingsHot stamping/Roll leafInformation provided by Mitsubishi Polyester Film
Physical Properties Metric English Comments
Density 1.40 g/cc

@Temperature 23.0 °C
0.0506 lb/in³

@Temperature 73.4 °F
ASTM D1505-68, method C
Linear Mold Shrinkage 0.013 cm/cm

@Temperature 150 °C,
Time 900 sec
0.013 in/in

@Temperature 302 °F,
Time 0.250 hour
DIN 40634
Linear Mold Shrinkage, Transverse 0.0030 cm/cm

@Temperature 150 °C,
Time 900 sec
0.0030 in/in

@Temperature 302 °F,
Time 0.250 hour
DIN 40634
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 260 MPa
37700 psi
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD 265 MPa
38400 psi
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD >= 130 %
>= 130 %
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD 100 %
100 %
Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity 4.40 GPa

@Temperature 23.0 °C
638 ksi

@Temperature 73.4 °F
MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
5.00 GPa

@Temperature 23.0 °C
725 ksi

@Temperature 73.4 °F
TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static 0.40
0.40
DIN 53375 or ASTM D1894
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
Enlarged measurement angle; ASTM D1003-61, method A
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Descriptive Properties Value Comments
F5-value (MPa) 105
ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23ºC, 50% r.h.
110
ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23ºC, 50% r.h.