- MetalTek RENE® 220 Centri-Vac Nickel Cobalt Based Alloy
MetalTek RENE® 220 Centri-Vac Nickel Cobalt Based Alloy
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | MetalTek |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MetalTek RENE® 220 Centri-Vac Nickel Cobalt Based Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by MetalTekWrought Grade RENE® 220
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | >= 1105 MPa | >= 160300 psi | |
| Tensile Strength, Yield | >= 830 MPa | >= 120000 psi | |
| Elongation at Break | >= 6.0 % | >= 6.0 % |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.020 - 0.040 % | 0.020 - 0.040 % | |
| Chromium, Cr | 18 - 22 % | 18 - 22 % | |
| Cobalt, Co | 11 - 13 % | 11 - 13 % | |
| Molybdenum, Mo | 3.0 - 3.4 % | 3.0 - 3.4 % | |
| Nickel, Ni | 51.46 - 59.08 % | 51.46 - 59.08 % | As Balance |
| Niobium, Nb (Columbium, Cb) | 5.0 - 5.5 % | 5.0 - 5.5 % | |
| Tantalum, Ta | 3.0 - 3.5 % | 3.0 - 3.5 % | |
| Titanium, Ti | 0.90 - 1.1 % | 0.90 - 1.1 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Treatment | Sol. Anneal & Age |
Users viewing this material also viewed the following:
- Fiberfil® J-60/30/F Polypropylene Homopolymer, 30% Glass Reinforced, Chemically coupled
- SABIC Innovative Plastics NORYL PPX PPX7115 PPE+PP (Europe-Africa-Middle East)
- Universal Wire Works EZ33A (AMS 4396) Magnesium Alloy Filler Metal
- EMS-Griltech Grilamid® DN 80 Nylon 12 Monofilament
- Ametek P409L/409CB P/M Stainless Steel, Sintered from 6.60 g/cc Green Density
- Bhansali Engineering Abstron IM-11 ABS Injection Molding Grade
- Aclo Accutech SAN SAN930G40L Glass Reinforced
- 3A Composites Core Materials AIREX® C71.55 Elevated Temperature Structural Foam
Copyright © lookpolymers.com All Rights Reserved