Metabolix Mirelâ„¢ P4001 Sheet Extrusion Grade Bioplastic

Category Polymer , Renewable/Recycled Polymer , Thermoplastic
Manufacturer Metabolix
Trade Name Mirel™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Metabolix Mirelâ„¢ P4001 Sheet Extrusion Grade Bioplastic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Mirelâ„¢ P4001 is a general purpose, high melt strength material suitable for cast sheet extrusion. Mirelâ„¢ P4001 is designed for a wide range of sheet applications including gift cards, promotional materials, indoor/outdoor signage, plant pots and plant tags. Mirelâ„¢ P4001 can be processed on conventional extrusion equipment with either an up-stack or down-stack roll configuration.
Physical Properties Metric English Comments
Specific Gravity 1.40 g/cc
1.40 g/cc
ASTM D792
Viscosity 1200 cP

@Shear Rate 100 1/s,
Temperature 180 °C
1200 cP

@Shear Rate 100 1/s,
Temperature 356 °F
Melt
Mechanical Properties Metric English Comments
Tensile Strength, Yield 20.0 MPa
2900 psi
ASTM D638
Elongation at Break 5 %
5 %
ASTM D638
Flexural Modulus 1.90 GPa
276 ksi
ASTM D790 A
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256 A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ASTM D648 B
Deflection Temperature at 1.8 MPa (264 psi) 57.0 °C
135 °F
ASTM D648 B
Vicat Softening Point 133 °C
271 °F
ASTM 1525 B10
Processing Properties Metric English Comments
Rear Barrel Temperature 175 °C
347 °F
Reverse Temperature Profile
Middle Barrel Temperature 170 °C
338 °F
Front Barrel Temperature 165 °C
329 °F
Die Temperature 165 °C
329 °F
Center
165 °C
329 °F
Edge Zones
Melt Temperature 165 - 170 °C
329 - 338 °F
Drying Temperature 80.0 °C

@Time 14400 sec
176 °F

@Time 4.00 hour
Desiccant