Materion Beryllium Copper Alloy 3 Strip; AT (TF00) Temper (UNS C17510)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 3 Strip; AT (TF00) Temper (UNS C17510).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: 2-3 hrs @ 480ºC or Mill HardenedStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 94%Stress Relaxation after 1000 hrs @ 200°C: 72%Formability Ratio, 90° Bend, Radius/Thickness (Good Way): 1Formability Ratio (bad Way): 1Superficial Hardness: 30T 77-82Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.83 g/cc | 0.319 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 92 - 100 | 92 - 100 | |
| Hardness, Vickers | 195 - 275 | 195 - 275 | |
| Tensile Strength, Ultimate | 680 - 900 MPa | 98600 - 131000 psi | |
| Tensile Strength, Yield | 550 - 690 MPa | 79800 - 100000 psi | |
| Elongation at Break | 10 - 25 % | 10 - 25 % | |
| Modulus of Elasticity | 138 GPa | 20000 ksi | |
| Fatigue Strength | 260 - 300 MPa @# of Cycles 1.00e+8 |
37700 - 43500 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 18.0 µm/m-°C @Temperature 20.0 - 200 °C |
10.0 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 240 W/m-K | 1670 BTU-in/hr-ft²-°F | |
| Melting Point | 1040 - 1080 °C | 1900 - 1980 °F | |
| Solidus | 1040 °C | 1900 °F | |
| Liquidus | 1080 °C | 1980 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 0.20 - 0.60 % | 0.20 - 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Nickel, Ni | 1.4 - 2.2 % | 1.4 - 2.2 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000290 - 0.00000380 ohm-cm | 0.00000290 - 0.00000380 ohm-cm | 45-60% IACS Conductivity |
Users viewing this material also viewed the following:
- Polimeri Europa Greenflex® ML 30 Ethylene Vinyl Acetate Copolymer - Injection Molding & Profile Extrusion
- DuPont Appeel® LSR 11D569 Modified EVA Lidding Sealing Resin (discontinued **)
- MarkeTech Zinc Oxide (ZnO) Single Crystal Substrate
- LG Chemical KEYFLEX BT 1072D Ester Type TPE
- Samsung Cheil Industries Infino® PCA-NH1015V Flame Retardant
- PlastxWorld CEVIAN® S1210 PC/ABS alloy
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 65A
- Ensinger Hydel® PC-P ESD Polycarbonate (PC)
- DuPont Performance Polymers Hytrel® HTR8785 BK482 Polyester Elastomer TPC-ET (Unverified Data**)
- Plenco 7552 Phenolic, Nodular, Transfer Molded
Copyright © lookpolymers.com All Rights Reserved