- Materion Beryllium Copper Alloy 25 Strip; 1/2HT (TH02) Temper (UNS C17200)
Materion Beryllium Copper Alloy 25 Strip; 1/2HT (TH02) Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 25 Strip; 1/2HT (TH02) Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: 2 hrs @ 315ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 97%Stress Relaxation after 1000 hrs @ 200°C: 73%Superficial Hardness: 30N 58-63Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 38 - 44 | 38 - 44 | |
| Hardness, Vickers | 373 - 435 | 373 - 435 | |
| Tensile Strength, Ultimate | 1270 - 1490 MPa | 184000 - 216000 psi | |
| Tensile Strength, Yield | 1100 - 1320 MPa | 160000 - 191000 psi | |
| Elongation at Break | 1.0 - 8.0 % | 1.0 - 8.0 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 290 - 320 MPa @# of Cycles 1.00e+8 |
42100 - 46400 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000610 - 0.00000780 ohm-cm | 0.00000610 - 0.00000780 ohm-cm | 22-28% IACS Conductivity |
Users viewing this material also viewed the following:
- Parker Chomerics Tecknit Teckfip™ FIP-N Formed in Place Conductive Elastomer
- Lucent Polymers PC-FR0 Polycarbonate, Flame Resistant
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- American Elements Terbium Oxide Nanopowder
- American Elements Zirconium Oxide Nanopowder
- DSM Akulon® F223-D (Dry) Low/Medium Viscosity Nylon 6 (North America)
- ExxonMobil Vistalon™ 878P Ethylene Propylene Copolymer Rubber
- Aclo Accutech Polypropylene Homopolymer HP0339C40L Calcium Reinforced
- A. Schulman LP642 Narrow Molecular Weight Copolymer, High-Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved