Master Bond Supreme 10HTND-3 Non-Drip Epoxy Resists High Temperatures

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Master Bond Inc.
Trade Name Supreme
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond Supreme 10HTND-3 Non-Drip Epoxy Resists High Temperatures.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Master Bond Supreme 10HTND-3 features a blend of performance properties including both high shear and peel strengths along with a totally non-drip application feature. This one component system is formulated to cure at elevated temperatures, e.g. 60-75 minutes at 250°F. Tensile shear strengths of 3,600 psi and T-peel strengths up to 30 pli are readily obtained. Supreme 10HTND-3 has a number of processing advantages; no mixing is necessary prior to use, the viscosity remains constant with time (i.e. it will not thicken over time), the working life is unlimited at room temperature and it is room temperature storable. This epoxy is cryogenically serviceable and has a wide temperature range of 4K to +400°F. Master Bond Supreme 10HTND-3 readily withstands severe thermal cycling along with mechanical shock and vibration. It is very resistant to many chemicals including water, oils, fuels, solvents, acids and bases. It has excellent adhesion to metals, glass, ceramics and many plastics. The cured epoxy is a superior electrical insulator. Its natural color is gray, but other colors are available. Its viscosity is pastelike and has no flow at all when cured. Supreme 10HTND-3’s high performance properties coupled with its convenient handling make it widely used in a variety of applications in the aerospace, electronic, electrical, computer, metalworking, appliance, automotive and chemical industries. Product Advantages: Single component system; no mixing needed prior to use; no viscosity changes over time. Completely non-flow when applied and cured. Room temperature storable. Versatile cure schedules: 60-75 minutes at 250°F; 35-45 minutes at 300°F. High shear and peel strengths to a wide variety of similar and dissimilar substrates. Service temperature range of 4K to +400°F. Good electrical insulating properties and chemical resistance. Superior thermal cycling ability; resistance to mechanical and thermal shocks. 100% reactive; contains no solvents or diluents.Information provided by MasterBond®
Mechanical Properties Metric English Comments
Hardness, Shore D >= 70
>= 70
Tensile Strength at Break >= 51.7 MPa
>= 7500 psi
Elongation at Break >= 5.0 %
>= 5.0 %
Tensile Modulus >= 2.76 GPa
>= 400 ksi
Flexural Strength >= 68.9 MPa
>= 10000 psi
Compressive Strength >= 89.6 MPa
>= 13000 psi
Shear Strength >= 24.8 MPa
>= 3600 psi
Tensile, Al to Al
Peel Strength 4.38 - 5.26 kN/m
25.0 - 30.0 pli
T-peel, Al to Al
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 204 °C
400 °F
Minimum Service Temperature, Air -168 °C
-270 °F
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Processing Properties Metric English Comments
Cure Time 35.000 - 45.0 min

@Temperature 149 °C
0.58333 - 0.750 hour

@Temperature 300 °F
60.0 - 75.0 min

@Temperature 121 °C
1.00 - 1.25 hour

@Temperature 250 °F
Shelf Life 3.00 - 6.00 Month

@Temperature 23.9 °C
3.00 - 6.00 Month

@Temperature 75.0 °F
in original unopened containers