Master Bond EP42HT-2 Epoxy Adhesive Resists Sterilization

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Master Bond Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond EP42HT-2 Epoxy Adhesive Resists Sterilization.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Master Bond Polymer System EP42HT-2 is a room temperature curable, two component epoxy adhesive, sealant, coating and casting material featuring high temperature resistance along with outstanding chemical resistance. While EP42HT-2 is a superior adhesive, sealant and coating, it is also relatively low in exotherm and castable up to 2-3 inches thick. EP42HT-2 cures readily at ambient temperatures or more quickly at elevated temperatures. A desirable cure schedule to optimize its properties is overnight at room temperature followed by 2-4 hours at 150-200°F. EP42HT-2 has an easy to use 100 to 40 mix ratio by weight or 100 to 50 by volume. It is resistant to a wide variety of acids, bases, solvents, fuels, oils and salts. It also has excellent electrical insulation properties. Its service temperature range is from -60°F to 450°F. EP42HT-2 is used in electronic, electrical, fiber-optic, optical and OEM type applications. The color of Part A is clear and Part B is amber. The system has superior optical transmission properties, particularly in thinner sections, as well as a high index of refraction for an epoxy. Product Advantages: Non-critical 100 to 40 mix ratio by weight or 100 to 50 by volume Easy application: only contact pressure required while curing; adhesive spreads readily Excellent chemical resistance to acids, alkalis and many solvents Castable up to thicknesses of 2-3 inches Outstanding physical strength properties Superior optical transmission properties Contains no solventsKey Features Heat, chemical and steam resistance Cures at ambient or elevated temperatures Can be used for bonding, sealing, coating, casting & potting applications Serviceable from -60°F to 450°FInformation provided by MasterBond®
Physical Properties Metric English Comments
Viscosity 30 - 70 cP

@Temperature 23.9 °C
30 - 70 cP

@Temperature 75.0 °F
Part B
1000 - 1800 cP

@Temperature 52.2 °C
1000 - 1800 cP

@Temperature 126 °F
Part A
55000 - 110000 cP

@Temperature 23.9 °C
55000 - 110000 cP

@Temperature 75.0 °F
Part A
Mechanical Properties Metric English Comments
Hardness, Shore D >= 75
>= 75
Tensile Strength at Break >= 82.7 MPa
>= 12000 psi
Elongation at Break <= 5.0 %
<= 5.0 %
Tensile Modulus 2.41 - 2.76 GPa
350 - 400 ksi
Shear Strength >= 13.8 MPa
>= 2000 psi
Tensile lap, Al to Al
Thermal Properties Metric English Comments
CTE, linear 35.0 - 40.0 µm/m-°C
19.4 - 22.2 µin/in-°F
Maximum Service Temperature, Air 232 °C
450 °F
Minimum Service Temperature, Air -51.1 °C
-60.0 °F
Optical Properties Metric English Comments
Refractive Index 1.63
1.63
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
Dielectric Constant 3.8

@Frequency 60.0 Hz,
Temperature 25.0 °C
3.8

@Frequency 60.0 Hz,
Temperature 77.0 °F
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 93.3 °C
2.00 - 3.00 hour

@Temperature 200 °F
2880 - 4320 min

@Temperature 23.9 °C
48.0 - 72.0 hour

@Temperature 75.0 °F
Pot Life 45 - 75 min
45 - 75 min
100 gram batch
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
in original unopened container
Descriptive Properties Value Comments
Mixing Ratio (A to B) 100:40
by weight
100:50
by volume