Master Bond EP42-2LV Epoxy Resists Heat and Chemicals

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond EP42-2LV Epoxy Resists Heat and Chemicals.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Master Bond Polymer System EP42-2LV is a low viscosity room temperature curable two component epoxy, adhesive, sealant, coating and casting material featuring outstanding chemical resistance. While EP42-2LV is a superior adhesive, sealant and coating, it is also castable to thicknesses exceeding 2-3 inches. EP42-2LV cures readily at ambient or more quickly at elevated temperatures. One particularly effective cure schedule is overnight at room temperature followed by 2-4 hours at 150-200°F. It has an easy to use 100 to 40 mix ratio by weight or 100 to 50 by volume. One salient property regarding this system is unlike most low viscosity, room temperature curing epoxies, EP42-2LV excels in chemical resistance. The cured material is resistant to various types of inorganic and organic acids, alkalis, solvents, aromatic hydrocarbons, fuels and oils. EP42-2LV is an excellent electrical insulator. Its serviceability from -60°F up to 300°F is especially noteworthy. Its low viscosity enables it to be particularly desirable for potting and encapsulations as well as coatings. Part A is clear in color and the color of Part B is amber. EP42-2LV is also used in aerospace, electronics, electrical, fiber-optic and optical as well as OEM type applications. Product Advantages: Convenient, non-critical 100 to 40 mix ratio by weight or 100 to 50 by volume. Contains no solvents or volatiles. Convenient cure schedules at both ambient and elevated temperatures. Excellent chemical resistance to acids, bases and many solvents. Castable to thicknesses up to 2-3 inches. Service temperature range of -60°F to 300°F. Bonds well to a wide variety of substrates. Outstanding physical strength properties. Especially noteworthy for combining low viscosity and exceptional chemical resistance.Information provided by MasterBond®
Physical Properties Metric English Comments
Viscosity 30 - 70 cP
30 - 70 cP
Part B
10000 - 14000 cP
10000 - 14000 cP
Part A
Mechanical Properties Metric English Comments
Hardness, Shore D >= 75
>= 75
Tensile Strength at Break >= 68.9 MPa
>= 10000 psi
Elongation at Break 3.4 %
3.4 %
Tensile Modulus >= 2.76 GPa
>= 400 ksi
Shear Strength >= 13.8 MPa
>= 2000 psi
Tensile lap, Al to Al
Thermal Properties Metric English Comments
CTE, linear 35.0 - 40.0 µm/m-°C
19.4 - 22.2 µin/in-°F
Maximum Service Temperature, Air 149 °C
300 °F
Minimum Service Temperature, Air -51.1 °C
-60.0 °F
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
Dielectric Constant 3.8

@Frequency 60.0 Hz,
Temperature 25.0 °C
3.8

@Frequency 60.0 Hz,
Temperature 77.0 °F
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 93.3 °C
2.00 - 3.00 hour

@Temperature 200 °F
2880 - 4320 min

@Temperature 23.9 °C
48.0 - 72.0 hour

@Temperature 75.0 °F
Pot Life 60 - 90 min
60 - 90 min
100 gram batch
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
in original unopened container
Descriptive Properties Value Comments
Mixing Ratio (A to B) 100:40
by weight
100:50
by volume