Master Bond EP41SMed Two Component, Low Viscosity, USP Class VI Epoxy System
| Category | Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced , Epoxy, Cast, Unreinforced |
| Manufacturer | Master Bond Inc. |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Master Bond EP41SMed Two Component, Low Viscosity, USP Class VI Epoxy System.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Master Bond Polymer Adhesive EP41S Medical is a two component low viscosity epoxy resin system for high performance bonding, sealing, coating, as well as small encapsulations, pottings and castings. It is formulated to cure readily at room temperature or more quickly at elevated temperatures. One notable property is its very fast curing at room temperature. EP41S Medical meets USP Class VI specifications, making it well suited for a variety of uses in medical devices as an adhesive, sealant and coating.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 4000 - 6000 cP | 4000 - 6000 cP | Part B |
| 8000 - 10000 cP | 8000 - 10000 cP | mixed compound | |
| 10000 - 14000 cP | 10000 - 14000 cP | Part A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 68.9 MPa | >= 10000 psi | |
| Tensile Modulus | 2.76 GPa | 400 ksi | |
| Adhesive Bond Strength | >= 17.9 MPa | >= 2600 psi | after 30 days water absorption |
| >= 18.6 MPa | >= 2700 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 121 °C | 250 °F | |
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | |
| Dielectric Strength | >= 17.3 kV/mm @Thickness 3.17 mm |
>= 440 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 100 °C |
1.00 hour @Temperature 212 °F |
|
| 1440 min @Temperature 23.9 °C |
24.0 hour @Temperature 75.0 °F |
||
| Pot Life | 10 - 15 min | 10 - 15 min | 100 gram mass |
| Shelf Life | 6.00 Month | 6.00 Month | in unopened containers |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mixing Ratio (A to B) | 5/1 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Q50Y Polyurethane Rubber
- Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1120°C for 5 minutes
- IRPC Polimaxx Polene 1100NN Polypropylene Homopolymer
- Samsung Cheil Industries Infino® VB-8102G MPPE, Glass Filled FR
- Teknor Apex Telcar® TL-1336B Thermoplastic Elastomer
- Polyplastics Duranex® H7500 Polybutylene Terephthalate (PBT), Low warpage
- A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6000 HWCP Nylon 6, Heat Stabilized, Dry
- EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45
Copyright © lookpolymers.com All Rights Reserved