Master Bond EP36CLV One Component Heat Resistant Liquid Flexible Epoxy

Category	Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced , Epoxy, High Temperature
Manufacturer	Master Bond Inc.
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Master Bond EP36CLV One Component Heat Resistant Liquid Flexible Epoxy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Master Bond Polymer System EP36CLV is a one component, high temperature resistant, B staged epoxy that cures with excellent toughness and is far less rigid than typical high temperature resistant epoxies. It is serviceable for temperatures up to 500°F and is used primarily for potting and encapsulation applications. EP36CLV is semi-solid at room temperature and requires heating by ramping up the temperature slowly to 160-180°F. Once liquefied, it is applied while hot to the encapsulation and then cured for 4-8 hours at 350°F.

Physical Properties	Metric	English
Density	1.18 g/cc	0.0426 lb/in³
Water Absorption	0.30 %	0.30 %
Viscosity	500 - 1000 cP @Temperature 82.2 °C	500 - 1000 cP @Temperature 180 °F

Mechanical Properties	Metric	English
Hardness, Shore D	20 @Temperature 100 °C	20 @Temperature 212 °F
	40 @Temperature 25.0 °C	40 @Temperature 77.0 °F
Tensile Strength	58.6 MPa	8500 psi
Flexural Strength	121 MPa	17600 psi
Izod Impact, Notched	0.481 J/cm	0.900 ft-lb/in

Thermal Properties	Metric	English
CTE, linear	51.0 µm/m-°C	28.3 µin/in-°F
Maximum Service Temperature, Air	260 °C	500 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F
Shrinkage	>= 2.0 %	>= 2.0 %

Processing Properties	Metric	English	Comments
Cure Time	240 - 480 min @Temperature 177 °C	4.00 - 8.00 hour @Temperature 350 °F
Shelf Life	12.0 Month	12.0 Month	in original unopened containers

Descriptive Properties	Value	Comments
Heat Stability	Negligible change in electrical properties after 1000 hrs at 200°C
Thermal Shock Resistance	excellent	-65°C - 150°C
Viscosity	Solid	75°F