Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound

Category Polymer , Thermoset , Epoxy , Epoxy Encapsulant, Unreinforced
Manufacturer Master Bond Inc.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Master Bond EP21TDC-2ND is a two component highly flexible epoxy resin system for high performance bonding, sealing and coating with a non-drip consistency. It has a forgiving one to three mix ratio by weight. The system is formulated to cure fully at ambient temperature or more quickly at elevated temperatures. The optimum cure schedule is overnight at room temperature followed by 2-3 hours at 150-200°F. An unusual feature here is that the curing cycle can affect the hardness of the system. If cured only at elevated temperatures, the Shore A hardness is 50-55. If cured with the optimum cure schedule, the Shore A is 75-80. It has very high peel strength and elongation. EP21TDC-2ND develops very little exotherm while curing, making it well suited for sealing or encapsulating in thicker sections. It has excellent adhesion to a wide array of substrates including metals, composites, glass, ceramics and many rubbers and plastics. Its flexibility allows EP21TDC-2ND to have excellent thermal cycling properties along with exceptional resistance to thermal and mechanical shock and vibration. This epoxy is a superb electrical and thermal insulator with good resistance to chemicals such as water, oils, hydraulic fluids, bases and salts. EP21TDC-2ND is cryogenically serviceable and has a temperature range of 4K to +250°F. EP21TDC-2ND is widely used in aerospace, specialty OEM, optical and especially applications where robust thermal cycling properties and shock resistance are paramount. Product Advantages: Easy application: paste-like consistency; non-drip Cures readily at ambient temperature or faster at elevated temperatures Variable hardness and flexibility depending upon cure schedule Bonds well to a wide variety of substrates Excellent peel strength, dependable resistance to rigorous thermal cycling Cryogenic serviceabilityInformation provided by MasterBond®
Mechanical Properties Metric English Comments
Hardness, Shore D 50 - 55
50 - 55
cured at 150-200°F
75 - 80
75 - 80
cured with optimum schedule
Tensile Strength at Break >= 34.5 MPa

@Temperature 23.9 °C
>= 5000 psi

@Temperature 75.0 °F
Elongation at Break <= 120 %
<= 120 %
Shear Strength >= 8.27 MPa

@Temperature 23.9 °C
>= 1200 psi

@Temperature 75.0 °F
Al/Al, Tensile lap
Peel Strength >= 5.26 kN/m
>= 30.0 pli
T-peel
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 121 °C
250 °F
Minimum Service Temperature, Air -269 °C
-452 °F
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
Processing Properties Metric English Comments
Cure Time 120 - 180 min

@Temperature 93.3 °C
2.00 - 3.00 hour

@Temperature 200 °F
720 min

@Temperature 23.9 °C
12.0 hour

@Temperature 75.0 °F
Followed by 2-3 hours at 150-200°F (Optimum Cure Schedule)
2880 - 4320 min

@Temperature 23.9 °C
48.0 - 72.0 hour

@Temperature 75.0 °F
Pot Life >= 60 min
>= 60 min
100 gram mass
Shelf Life 12.0 Month

@Temperature 23.9 °C
12.0 Month

@Temperature 75.0 °F
in original unopened containers
Descriptive Properties Value Comments
Mixing Ratio (A to B) 1:3
by weight