Mapal Plastics Maplon Type H Polypropylene Sheet
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade |
| Manufacturer | Mapal Plastics |
| Trade Name | Maplon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mapal Plastics Maplon Type H Polypropylene Sheet.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties : Good resistance to low temperatures, Moderate stress whitening, Suitable for die cutting, Corona treated on both sides for offset and screen printing.Applications : Stationery, Printing and packaging products, Industrial applications where low temperature resistance is required
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.910 g/cc | 0.910 g/cc | |
| Thickness | 1000 microns | 39.4 mil | |
| Surface Tension | >= 48 dynes/cm | >= 48 dynes/cm | Special grade can be treated for more than year for offset printing |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 29.0 MPa @Temperature 23.0 °C |
4210 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Tensile Strength at Yield, TD | 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, MD | >= 200 % @Temperature 23.0 °C |
>= 200 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Break, TD | >= 100 % @Temperature 23.0 °C |
>= 100 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, MD | 18 % @Temperature 23.0 °C |
18 % @Temperature 73.4 °F |
ASTM D638 |
| Film Elongation at Yield, TD | 14 % @Temperature 23.0 °C |
14 % @Temperature 73.4 °F |
ASTM D638 |
| Modulus of Elasticity | 0.400 GPa @Temperature 23.0 °C |
58.0 ksi @Temperature 73.4 °F |
MD/TD; ASTM D638 |
| Izod Impact, Notched | 3.00 J/cm @Thickness 3.20 mm, Temperature 0.000 °C |
5.62 ft-lb/in @Thickness 0.126 in, Temperature 32.0 °F |
ASTM D256 |
| 5.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
9.37 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 2.00 J @Temperature -20.0 °C |
1.48 ft-lb @Temperature -4.00 °F |
ASTM D1709-85 |
| 5.50 J @Temperature 0.000 °C |
4.06 ft-lb @Temperature 32.0 °F |
ASTM D1709-85 | |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D1709-85 | |
| Dart Drop Total Energy | 20.0 J/cm @Temperature -20.0 °C |
0.0375 ft-lb/mil @Temperature -4.00 °F |
|
| 55.0 J/cm @Temperature 0.000 °C |
0.103 ft-lb/mil @Temperature 32.0 °F |
||
| 60.0 J/cm @Temperature 23.0 °C |
0.112 ft-lb/mil @Temperature 73.4 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 145 °C | 293 °F | ASTM D1525 |
| Heat Distortion Temperature | 85.0 °C | 185 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Mapal Color Catalogue No. 520002 |