Manifattura Cattaneo PA 6 Nylon
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Manifattura Cattaneo spa |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Manifattura Cattaneo PA 6 Nylon.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 3.0 % @Temperature 23.0 °C |
3.0 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 9.5 % | 9.5 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85 | 85 | ISO 2039-2 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | Conditioned 50% RH; ISO 527 |
| 90.0 MPa | 13100 psi | Dried; ISO 527 | |
| Elongation at Break | >= 50 % | >= 50 % | Conditioned 50% RH; ISO 527 |
| Elongation at Yield | 4.5 % | 4.5 % | Dried; ISO 527 |
| 20 % | 20 % | Conditioned 50% RH; ISO 527 | |
| Tensile Modulus | 1.00 GPa | 145 ksi | Conditioned 50% RH; ISO 527 |
| 3.00 GPa | 435 ksi | Dried; ISO 527 | |
| Compressive Yield Strength | 24.0 MPa @Strain 1.00 % |
3480 psi @Strain 1.00 % |
ISO 604 |
| Poissons Ratio | 0.38 | 0.38 | Dried |
| 0.45 | 0.45 | Conditioned 50% RH | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Dried; ISO 179 |
| NB | NB | Conditioned 50% RH; ISO 179 | |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | on polished steel; MPC Test |
| Coefficient of Friction, Static | 0.22 | 0.22 | on polished steel; MPC Test |
| K Factor (Wear Factor) | 8.5 | 8.5 | µm/s. PV = 0.1 MPa-m/s; max P = 24 MPa; MPC Test |
| Limiting Pressure Velocity | 0.0700 MPa-m/sec | 2000 psi-ft/min | without lubrication; MPC Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 85.0 µm/m-°C @Temperature 23.0 - 100 °C |
47.2 µin/in-°F @Temperature 73.4 - 212 °F |
ASTM D696 |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | DOM 52612 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Dried; ISO 75 |
| 180 °C | 356 °F | Conditioned 50% RH; ISO 75 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Dried; ISO 75 |
| 90.0 °C | 194 °F | Conditioned 50% RH; ISO 75 | |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Oxygen Index | 25 % | 25 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | IEC 60094 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 16.0 kV/mm @Thickness 2.00 mm |
406 kV/in @Thickness 0.0787 in |
IEC 60243 |
| Dielectric Loss Index | 0.060 @Frequency 1.00e+6 Hz |
0.060 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| White | ||
| UV Resistance | N |