Magnesium Elektron Elektron® 43 Magnesium Wrought Alloy

Category	Metal , Nonferrous Metal , Magnesium Alloy
Manufacturer	Magnesium Elektron
Trade Name	Elektron®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Magnesium Elektron Elektron® 43 Magnesium Wrought Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High strength wrought Mg alloy available as rolled plate, forging feedstock, and extrusions. It is a wrought evolution of the casting alloy Elektron WE43. Elektron 43 uses zirconium grain refining and has successfully undergone flammability tests by the FAA for use in aircraft seat frames. It develops maximum strength in the T5 condition.

Physical Properties	Metric	English	Comments
Density	1.84 g/cc	0.0665 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Brinell	70 - 90	70 - 90
Tensile Strength	296 MPa	43000 psi	Extruded Bar - Transverse
	331 MPa	48000 psi	Extruded Bar - Longitudinal
	345 MPa @Thickness 1.02 - 38.1 mm	50000 psi @Thickness 0.0400 - 1.50 in	Rolled Plate
	345 MPa @Thickness 38.13 - 76.2 mm	50000 psi @Thickness 1.501 - 3.00 in	Rolled Plate
Tensile Strength, Yield	179 MPa @Strain 0.200 %	26000 psi @Strain 0.200 %	Extruded Bar - Transverse
	214 MPa @Strain 0.200 %	31000 psi @Strain 0.200 %	Extruded Bar - Longitudinal
	255 MPa @Strain 0.200 %, Thickness 38.13 - 76.2 mm	37000 psi @Strain 0.200 %, Thickness 1.501 - 3.00 in	Rolled Plate
	276 MPa @Strain 0.200 %, Thickness 1.02 - 38.1 mm	40000 psi @Strain 0.200 %, Thickness 0.0400 - 1.50 in	Rolled Plate
Elongation at Break	11 %	11 %	Extruded Bar - Transverse
	14 %	14 %	Extruded Bar - Longitudinal
	12 % @Thickness 1.02 - 38.1 mm	12 % @Thickness 0.0400 - 1.50 in	Rolled Plate
	14 % @Thickness 38.13 - 76.2 mm	14 % @Thickness 1.501 - 3.00 in	Rolled Plate
Modulus of Elasticity	44.0 GPa	6380 ksi
Poissons Ratio	0.27	0.27
Fatigue Strength	186 MPa @# of Cycles 5.00e+7	27000 psi @# of Cycles 5.00e+7	Axial; R = 0.1; Extruded Bar; ASTM E466
Shear Modulus	17.3 GPa	2510 ksi	Calculated

Thermal Properties	Metric	English
CTE, linear	26.7 µm/m-°C	14.8 µin/in-°F
	26.7 µm/m-°C	14.8 µin/in-°F
Specific Heat Capacity	0.966 J/g-°C	0.231 BTU/lb-°F
Thermal Conductivity	51.3 W/m-K	356 BTU-in/hr-ft²-°F
Melting Point	540 - 640 °C	1000 - 1180 °F
Solidus	540 °C	1000 °F
Liquidus	640 °C	1180 °F
Maximum Service Temperature, Air	249 °C	480 °F

Component Elements Properties	Metric	English	Comments
Magnesium, Mg	92 - 93.8 %	92 - 93.8 %	as balance
Rare Earths	2.3 - 3.5 %	2.3 - 3.5 %
Yttrium, Y	3.7 - 4.3 %	3.7 - 4.3 %
Zirconium, Zr	>= 0.20 %	>= 0.20 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.0000148 ohm-cm	0.0000148 ohm-cm

Descriptive Properties	Value	Comments
Damping Index	0.09