MRC Polymers NAXELLâ„¢ PC429MHI Polycarbonate, Impact Modified

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer	MRC Polymers
Trade Name	NAXELL™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	MRC Polymers NAXELLâ„¢ PC429MHI Polycarbonate, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

â€¢ Medium MFRâ€¢ Good property retention, heat and dimensional stabilityâ€¢ Available in natural and custom colorsâ€¢ Can be UV Stabilizedâ€¢ Internal and external lubricants can be addedInformation provided by MRC Polymers Inc.

Physical Properties	Metric	English	Comments
Specific Gravity	1.19 g/cc	1.19 g/cc	ISO 1183-1A
Linear Mold Shrinkage	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in	ASTM D 955
Melt Flow	12 g/10 min @Load 1.20 kg, Temperature 300 Â°C	12 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	58.0 MPa	8410 psi	ISO 527
Flexural Strength	86.0 MPa	12500 psi	ISO 178
Flexural Modulus	2.268 GPa	328.9 ksi	ISO 178
Izod Impact, Notched (ISO)	50.0 kJ/mÂ²	23.8 ft-lb/inÂ²	ISO 180
Impact Test	47.0 J @Temperature 23.0 Â°C	34.7 ft-lb @Temperature 73.4 Â°F	3.2 mm, 2.2m/s. Instrumented Impact; ASTM D 3763
	48.0 J @Temperature -30.0 Â°C	35.4 ft-lb @Temperature -22.0 Â°F	3.2 mm, 2.2m/s. Instrumented Impact; ASTM D 3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	74.4 Âµm/m-Â°C @Temperature -30.0 - 100 Â°C	41.3 Âµin/in-Â°F @Temperature -22.0 - 212 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	78.1 Âµm/m-Â°C @Temperature -30.0 - 100 Â°C	43.4 Âµin/in-Â°F @Temperature -22.0 - 212 Â°F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	124 Â°C	255 Â°F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	118 Â°C	244 Â°F	ISO 75