MRC Polymers NAXALOYâ„¢ 793A3 GF10 PC and Polyester Blend, 10% Glass Fiber Filled

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled , Polyester, TP
Manufacturer MRC Polymers
Trade Name NAXALOY™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF MRC Polymers NAXALOYâ„¢ 793A3 GF10 PC and Polyester Blend, 10% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
793 GF10 is available in natural and custom colors, internal and external lubricants, UV stabilizer and other modifications.Information provided by MRC Polymers Inc.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm

@Thickness 3.17 mm
 0.0020 - 0.0050 in/in

@Thickness 0.125 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0070 cm/cm

@Thickness 3.17 mm
 0.0040 - 0.0070 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 68.9 MPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 10000 psi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D638
Elongation at Break 5.0 %

@Thickness 3.17 mm,
Temperature 22.8 °C
 5.0 %

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D638
Flexural Strength 103 MPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 15000 psi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D790
Flexural Modulus 3.10 GPa

@Thickness 3.17 mm,
Temperature 22.8 °C
 450 ksi

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D790
Izod Impact, Notched 1.33 J/cm

@Thickness 3.17 mm,
Temperature 22.8 °C
 2.50 ft-lb/in

@Thickness 0.125 in,
Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 °C

@Thickness 3.17 mm
 270 °F

@Thickness 0.125 in
 un-annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 110 °C

@Thickness 3.17 mm
 230 °F

@Thickness 0.125 in
 un-annealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 243 - 254 °C
470 - 490 °F
Middle Barrel Temperature 249 - 260 °C
480 - 500 °F
Front Barrel Temperature 254 - 266 °C
490 - 510 °F
Nozzle Temperature 257 - 268 °C
495 - 515 °F
Melt Temperature 260 - 277 °C
500 - 530 °F
Mold Temperature 37.8 - 93.3 °C
100 - 200 °F
Drying Temperature 104 - 121 °C
220 - 250 °F
Dry Time 6 - 8 hour
6 - 8 hour
Moisture Content <= 0.010 %
<= 0.010 %
Dew Point <= -17.8 °C
<= 0.000 °F
Drying Air Flow Rate 22.7 - 28.3 l/min
0.800 - 1.00 ft³/min (CFM)
per lb/hour resin processed
Injection Pressure 68.9 - 138 MPa
10000 - 20000 psi
Back Pressure 0.000 - 0.517 MPa
0.000 - 75.0 psi
Cushion 0.635 cm
0.250 in
Screw Speed 20 - 50 rpm
20 - 50 rpm
Descriptive Properties Value Comments
Fill Rate Moderate to Fast
Hold Pressure 40-60% of injection pressure
Packing Pressure 50-75% of injection pressure