MBA Polymers PP 2172 Post-consumer recycled polypropylene copolymer
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | MBA Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MBA Polymers PP 2172 Post-consumer recycled polypropylene copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High melt flow rate for injection molding applications. Available in standard black.Information provided by MBA Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | MBA Method |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C |
25 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.0 MPa @Temperature 23.0 °C |
2610 psi @Temperature 73.4 °F |
ISO 527-2/50 |
| Flexural Modulus | 0.900 GPa @Temperature 23.0 °C |
131 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | unannealed; ISO 75-1A |
| Vicat Softening Point | 58.0 °C | 136 °F | VST/B/50; ISO 306 |
| 136 °C | 277 °F | VST/A/50; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 210 °C | 356 - 410 °F | Extrusion Range |
| 200 °C | 392 °F | Recommended Extrusion | |
| 200 °C | 392 °F | Recommended Injection Molding | |
| 190 - 220 °C | 374 - 428 °F | Injection Molding Range | |
| Mold Temperature | 40.0 °C | 104 °F | Recommended |
| 30.0 - 60.0 °C | 86.0 - 140 °F | ||
| Drying Temperature | 80.0 °C @Time 3600 - 7200 sec |
176 °F @Time 1.00 - 2.00 hour |
|
| Moisture Content | <= 0.10 % | <= 0.10 % |