M. Holland Company LL104 LLDPE (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Blow Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	M. Holland Company LL104 LLDPE (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Butene Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2 and ASTM D 1248, I, Class A, Cat. 1Processing Method: Blown FilmInformation provided by M. Holland.

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in³	ASTM D1505
Thickness	31.8 microns	1.25 mil
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	570 %	570 %	ASTM D882
Film Elongation at Break, TD	760 %	760 %	ASTM D882
Secant Modulus, MD	0.228 GPa	33.1 ksi	1% Strain; ASTM D882
Secant Modulus, TD	0.283 GPa	41.0 ksi	1% Strain; ASTM D882
Coefficient of Friction	0.80	0.80	ASTM D1894
Elmendorf Tear Strength MD	190 g	190 g	ASTM D1922
Elmendorf Tear Strength TD	560 g	560 g	ASTM D1922
Dart Drop Test	80.0 g	0.176 lb	ASTM D1709
Film Tensile Strength at Break, MD	38.6 MPa	5600 psi	ASTM D882
Film Tensile Strength at Break, TD	27.6 MPa	4000 psi	ASTM D882

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 221 °C	360 - 430 °F
Blow-up Ratio (BUR)	1.5 - 2.5	1.5 - 2.5

Descriptive Properties	Value	Comments
Antiblock	Various
Form	Pellets
Slip	Various