LyondellBasell Ultrathene® UE637000 Ethylene Vinyl Acetate Copolymer, Film Extrusion Grade

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer LyondellBasell (former Equistar)
Trade Name Ultrathene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Ultrathene® UE637000 Ethylene Vinyl Acetate Copolymer, Film Extrusion Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ULTRATHENE UE637000 is an EVA copolymer with good toughness, flexibility and clarity. Applications include laminating and heavy duty films as well as injection and blow molding. UE637000 contains no additives.Regulatory Status: The basic copolymer UE637000 meets the requirements of the Food and Drug Administration regulations 21 CFR 177.1350 and 21 CFR 175.105. These regulations (respectively) allow for the use of this material as articles or components of articles which are "...intended for use in producing, manufacturing, packing, processing, preparing, treating, packaging, transporting or holding food..." and as an adhesive which "...may be safely used as components of articles intended for use in packaging, transporting or holding food." Specific limitations or conditions of use may apply. Please contact your Equistar sales representative for more information regarding the suitability of specific products for specific applications. Processing Techniques: The maximum recommended melt temperature for UE637000 is 430°F (221°C). Specific recommendations for processing UE637000 can only be made when the processing conditions, equipment and end use are known. For further suggestions, please contact your Equistar sales representative.This product is from the former Equistar product line.
Physical Properties Metric English Comments
Vinyl Acetate Content 9.0 %
9.0 %
Thickness 50.8 microns
2.00 mil
Melt Flow 3.2 g/10 min
3.2 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 94
94
ASTM D2240
Film Tensile Strength at Yield, MD 6.23 MPa
904 psi
ASTM D882
Film Tensile Strength at Yield, TD 5.81 MPa
843 psi
ASTM D882
Film Elongation at Break, MD 350 %
350 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Film Elongation at Yield, MD 9.0 %
9.0 %
ASTM D882
Film Elongation at Yield, TD 11 %
11 %
ASTM D882
Dart Drop 7.95 g/micron
202 g/mil
F<sub>50</sub>; ASTM D4272
Film Tensile Strength at Break, MD 25.9 MPa
3750 psi
ASTM D882
Film Tensile Strength at Break, TD 18.9 MPa
2740 psi
ASTM D882
1% Secant Modulus, MD 84.8 MPa
12300 psi
ASTM D882
1% Secant Modulus, TD 91.0 MPa
13200 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 80.0 °C
176 °F
ASTM D1525
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Processing Properties Metric English Comments
Melt Temperature <= 221 °C
<= 430 °F