LyondellBasell Moplen HP400N Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Moplen |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Moplen HP400N Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: HP400N is a high flow homopolymer with a conventional molecular weight distribution and is formulated with a general-purpose additive package. HP400N is designed for injection molding applications where ease of flow is important. It may also be used in conjunction with selected fillers. All ingredients in HP400N meet the chemical registration requirements of TSCA (U.S.) and DSL (Canada). Uses: Medical applications, packaging, containersInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 g/cc | 0.0325 lb/in³ | ASTM D792 & ISO 1183 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1183 |
| 12 g/10 min @Load 2.16 kg, Temperature 230 °C |
12 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 93 | 93 | ASTM D 785 |
| Hardness, Shore D | 73 | 73 | ISO 868 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ISO 527-1, -2 |
| 35.2 MPa | 5100 psi | ASTM D 638 | |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D 638 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
| 1.59 GPa | 230 ksi | 1% Secant, 0.05 in/min; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | 73°F; ASTM D256 |
| Izod Impact, Notched (ISO) | 2.50 kJ/m² | 1.19 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.1 °C | 124 °F | Unannealed; ISO 75A-1, -2 |
| Vicat Softening Point | 155 °C | 311 °F | Method A; ISO 306 |
| UL RTI, Electrical | 221 °C | 430 °F | 0.028 in; UL 746 |
| UL RTI, Mechanical with Impact | 221 °C | 430 °F | 0.028 in; UL 746 |
| UL RTI, Mechanical without Impact | 221 °C | 430 °F | 0.028 in; UL 746 |
| Flammability, UL94 | HB @Thickness 0.711 mm |
HB @Thickness 0.0280 in |
NC |