LyondellBasell Lupolen® 5361 A HDPE, Blow Molding Grade

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer LyondellBasell
Trade Name Lupolen®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LyondellBasell Lupolen® 5361 A HDPE, Blow Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Easy-to-process blow molding grade for stackable canisters (up to 60 l), used for packing surface-active liquids, laundry and dishwashing detergents, disinfectants, drums (up to 220 l) for various surface-active liquids and aggressive chemicals.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
Water Absorption 0.010 %
0.010 %
Moisture Absorption at Equilibrium 0.010 %
0.010 %
Melt Flow 0.10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
Mechanical Properties Metric English Comments
Tensile Strength, Yield 26.0 MPa
3770 psi
Elongation at Break >= 50 %
>= 50 %
Elongation at Yield 9.0 %
9.0 %
Tensile Modulus 1.00 GPa
145 ksi
Tensile Impact Strength 230 kJ/m²
109 ft-lb/in²
Tensile Creep Modulus, 1 hour 380 MPa
55100 psi
Tensile Creep Modulus, 1000 hours 270 MPa
39200 psi
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 155 µm/m-°C

@Temperature 20.0 °C
86.1 µin/in-°F

@Temperature 68.0 °F
Melting Point 133 °C
271 °F
Deflection Temperature at 0.46 MPa (66 psi) 76.0 °C
169 °F
Deflection Temperature at 1.8 MPa (264 psi) 45.0 °C
113 °F
Vicat Softening Point 80.0 °C
176 °F
Flammability, UL94 HB

@Thickness 0.400 mm
HB

@Thickness 0.0157 in
Oxygen Index 17 %
17 %
Electrical Properties Metric English Comments
Electrical Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
Dielectric Constant 2.4

@Frequency 100 Hz
2.4

@Frequency 100 Hz
2.4

@Frequency 1e+6 Hz
2.4

@Frequency 1e+6 Hz
Dielectric Strength 150 kV/mm
3810 kV/in
Dissipation Factor 0.00020

@Frequency 100 Hz
0.00020

@Frequency 100 Hz
0.00020

@Frequency 1e+6 Hz
0.00020

@Frequency 1e+6 Hz
Comparative Tracking Index 600 V
600 V