LyondellBasell Lupolen® 5261 ZS HDPE, Blow Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | LyondellBasell |
| Trade Name | Lupolen® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Lupolen® 5261 ZS HDPE, Blow Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Relatively high viscosity blow molding grade (similar to Lupolen 5261 Z), but more resistant to stress cracking) for rigid, stackable and highly shock resistant containers for packaging all types of hazardous materials.Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | |
| Water Absorption | 0.010 % | 0.010 % | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | |
| High Load Melt Index | 0.10 g/10 min @Load 21.6 kg, Temperature 190 °C |
0.10 g/10 min @Load 47.6 lb, Temperature 374 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 9.0 % | 9.0 % | |
| Tensile Modulus | 1.00 GPa | 145 ksi | |
| Tensile Impact Strength | 300 kJ/m² | 143 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 400 MPa | 58000 psi | |
| Tensile Creep Modulus, 1000 hours | 270 MPa | 39200 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 155 µm/m-°C @Temperature 20.0 °C |
86.1 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 133 °C | 271 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | |
| Vicat Softening Point | 78.0 °C | 172 °F | |
| Flammability, UL94 | HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
|
| Oxygen Index | 17 % | 17 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.4 @Frequency 100 Hz |
2.4 @Frequency 100 Hz |
|
| 2.4 @Frequency 1e+6 Hz |
2.4 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 150 kV/mm | 3810 kV/in | |
| Dissipation Factor | 0.00020 @Frequency 100 Hz |
0.00020 @Frequency 100 Hz |
|
| 0.00020 @Frequency 1e+6 Hz |
0.00020 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |