LyondellBasell Higlass PF072-2 Polypropylene Homopolymer, 20% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass PF072-2 Polypropylene Homopolymer, 20% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: conventional melt flow, medium high modulus, chemically coupled, glass fiber-reinforced polypropylene homopolymer, moderately high rigidity, high strength, good impact resistanceApplications: appliance parts, automotive components, pump housings, athletic equipmentDescription: Higlass PF072-2 high melt flow, chemically coupled, 20% glass fiber-reinforced polypropylene homopolymer has a very good balance of strength, stiffness and impact resistance.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	Tool, Montell
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	3.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	83.0 MPa	12000 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Modulus	4.50 GPa	653 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	0.850 J/cm	1.59 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	157 Â°C	315 Â°F	ASTM D648