LyondellBasell Higlass BJ44A Polypropylene Copolymer, 45% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass BJ44A Polypropylene Copolymer, 45% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: medium melt flow, high modulus, chemically coupled, glass fiber-reinforced polypropylene copolymer, high stiffness, good impact strength, excellent processabilityApplications: grille opening panels and reinforcements, headlamp retainersDescription: Higlass BJ44A medium melt flow, chemcially coupled, 45% glass fiber-reinforced polypropylene copolymer has excellent impact strength, high stiffnesss and very good processability. It was designe dprimariliy for automotive under-the-hood applications.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	1.26 g/cc	0.0455 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.0030 cm/cm	0.0030 in/in	Tool, Montell
Melt Flow	10 g/10 min @Load 2.16 kg, Temperature 230 Â°C	10 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	85.0 MPa	12300 psi	ASTM D638
Elongation at Break	6.0 %	6.0 %	ASTM D638
Elongation at Yield	3.0 %	3.0 %	ASTM D638
Flexural Modulus	7.00 GPa	1020 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	1.30 J/cm	2.44 ft-lb/in	ASTM D256A
Izod Impact, Unnotched	5.90 J/cm	11.1 ft-lb/in	ASTM D256A
Gardner Impact	5.00 J @Temperature -30.0 Â°C	3.69 ft-lb @Temperature -22.0 Â°F	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	145 Â°C	293 Â°F	ASTM D648