LyondellBasell Higlass BJ22GC Polypropylene Copolymer, 30% Glass Fiber

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	LyondellBasell
Trade Name	Higlass
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Higlass BJ22GC Polypropylene Copolymer, 30% Glass Fiber.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: conventional melt flow, medium high modulus, UV-stabilized, chemically coupled, glass fiber-reinforced polypropylene copolymer, moderately high rigidity, high impact strength, excellent weatherabilityApplications: splice enclosuresDescription: Higlass BJ22GC conventional melt flow, UV-staibilized, chemically coupled, 30% glass fiber-reinforced polypropylene copolymer was designed for applications which require high impact strength and extended outdoor exposure.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/inÂ³	ASTM D792
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 230 Â°C	3.0 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	55.0 MPa	7980 psi	ASTM D638
Elongation at Break	12 %	12 %	ASTM D638
Flexural Modulus	3.60 GPa	522 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	2.70 J/cm	5.06 ft-lb/in	ASTM D256A
Izod Impact, Unnotched	7.50 J/cm	14.1 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	153 Â°C	307 Â°F	ASTM D648