LyondellBasell Hifaxâ„¢ CB276 Thermoplastic Polyolefin Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifaxâ„¢ CB276 Thermoplastic Polyolefin Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hifaxâ„¢ CB276 very high melt flow, 1,200 MPa flexural modulus, UV-stabilized, precolored, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good combination of properties and processability. It was designed for exterior applications that require good cosmetics and undergo prolonged outdoor exposure. Uses: Automotive exterior partsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 230 °C |
30 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ISO 527-1, -2 |
| Elongation at Yield | 13 % | 13 % | ISO 527-1, -2 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.20 kJ/m² @Temperature -40.0 °C |
1.52 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 28.0 kJ/m² @Temperature 23.0 °C |
13.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Dart Drop, Total Energy | 21.0 J @Temperature 0.000 °C |
15.5 ft-lb @Temperature 32.0 °F |
Peak Energy, 135.0 m/min; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 100 °C |
38.9 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.2 °C | 171 °F | Unannealed; ISO 75B-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.8 °C | 118 °F | Unannealed; ISO 75A-1, -2 |
| Shrinkage | 0.70 % | 0.70 % | Tool, 100x150x3.2 mm; Basell Test Method |
| 1.10 % @Temperature 121 °C, Time 3600 sec |
1.10 % @Temperature 250 °F, Time 1.00 hour |
Afterbake, 100x150x3.2 mm; Basell Method |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CQX10030 R3 Polypropylene, Mineral Reinforced, Scratch Resistant
- Indium Corp. Indalloy® 233 Pb-Sb-Sn Solder Alloy
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane, 330ºF Cure Temperature
- A. Schulman POLYTROPE™ TPP 504E Extrusion Grade Olefinic Thermoplastic Elastomer
- ExxonMobil LD 302.56 High Clarity, High Impact Film Resin
- ConocoPhillips Hydroclear® 10W-30 Power-D E.O. 10W-30
- Solvay Specialty Polymers Algoflon® 25GL PTFE; Glass Fiber Filled (discontinued **)
- Gharda Chemicals Gafone™ B2315GF Polysupersulfone (PSS) (discontinued **)
- Latrobe MP159® Alloy
- Mitsui MILEX™ XL-1210MB Phenol Aralkyl Resin, Silicone Rubber Modified (discontinued **)
Copyright © lookpolymers.com All Rights Reserved