LyondellBasell Hifaxâ„¢ CA199AC Thermoplastic Olefin Resin

Category	Polymer , Thermoplastic
Manufacturer	LyondellBasell
Trade Name	Hifax™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LyondellBasell Hifaxâ„¢ CA199AC Thermoplastic Olefin Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Key Features: low melt flow, medium low modulus, paintable thermoplastic olefin resin, excellent balance of properties, high toughness, good paintability, flexibleApplications: automotive air bag door covers, closures and lid stockDescription: Hifax CA199AC low melt flow, paintable thermoplastic olein resin exhibits balanced strength, thoughness, flexibility and ductility. It is based on material produced from proprietary Montell process technology.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.

Physical Properties	Metric	English	Comments
Density	0.890 g/cc	0.0322 lb/inÂ³	ASTM D792
Linear Mold Shrinkage	0.010 cm/cm	0.010 in/in	Tool, Montell
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	2.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	52	52	ASTM D2240
Tensile Strength, Ultimate	12.0 MPa	1740 psi	ASTM D638
Tensile Strength, Yield	10.0 MPa	1450 psi	ASTM D638
Elongation at Break	400 %	400 %	ASTM D638
Elongation at Yield	22 %	22 %	ASTM D638
Flexural Modulus	0.340 GPa	49.3 ksi	Tangent at 0.05 in/min; ASTM D790A
Izod Impact, Notched	5.90 J/cm	11.1 ft-lb/in	ASTM D256A
Gardner Impact	21.0 J @Temperature -30.0 Â°C	15.5 ft-lb @Temperature -22.0 Â°F	ASTM D3029
Impact Test	21.0 J @Temperature -30.0 Â°C	15.5 ft-lb @Temperature -22.0 Â°F	Dynatup Impact, E at Max Load, Ductile; ASTM D3763