LyondellBasell Hifax™ CA186 Thermoplastic Olefin Resin
| Category | Polymer , Thermoplastic |
| Manufacturer | LyondellBasell |
| Trade Name | Hifax™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hifax™ CA186 Thermoplastic Olefin Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features: medium melt flow, medium modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, excellent paintability and paint durability, good processability, colorableApplications: fully painted and selectively decorated automotive bumper fascias, molded-color exterior componentsDescription: Hifax CA186 medium melt flow, reactor grade thermoplastic elastomeric olefin resin has an ecellent balance of impact, stiffnss and apintability. It is based on material produced from Montell's proprietary Catalloy process and was designed primarily for painted automotive bumper fascias that require high durability.Information provided by Montell Polyolefins.LyondellBasell is the successor company to Montell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | Tool, Montell |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 59 | 59 | ISO 868 |
| Tensile Strength, Ultimate | 16.0 MPa | 2320 psi | ISO R527-1 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ISO R527-1 |
| Elongation at Break | >= 500 % | >= 500 % | ISO R527-1 |
| Elongation at Yield | 15 % | 15 % | ISO R527-1 |
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ISO 178 |
| Izod Impact, Notched | 0.800 J/cm @Temperature -40.0 °C |
1.50 ft-lb/in @Temperature -40.0 °F |
ISO 180 |
| Impact Test | 22.0 J @Temperature -30.0 °C |
16.2 ft-lb @Temperature -22.0 °F |
MAII, E at Max Load, Ductile; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 110 µm/m-°C @Temperature -30.0 - 100 °C |
61.1 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | ISO 75 |