LyondellBasell Alathon® H5112 High Density Polyethylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Alathon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Alathon® H5112 High Density Polyethylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ALATHON H5112 is a medium-molecular-weight-distribution resin with balanced impact/ESCR and high flow characteristics. Typical applications include housewares, food containers, pail handles and toys. Regulatory Status: H5112 meets the requirements of the Food and Drug Administration regulation 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for more information. Specific recommendations for processing H5112 can only be made when the processing conditions, equipment and end use application are known.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in³ | ASTM D1895 |
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D1505 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C |
12 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Spiral Flow | 35.1 cm | 13.8 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 71 | 71 | ASTM D2240 |
| Tensile Strength at Break | 26.4 MPa | 3830 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 11 % | 11 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.7274 GPa | 105.5 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 0.8839 GPa | 128.2 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 0.9094 GPa | 131.9 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 1.092 GPa | 158.4 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.175 GPa | 170.4 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.299 J/cm | 0.560 ft-lb/in | ASTM D256 |
| NB @Temperature -18.0 °C |
NB @Temperature -0.400 °F |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 128.2 °C | 262.8 °F | ASTM D3418 |
| Crystallization Temperature | 114.2 °C | 237.6 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C2950 PC+ABS (Asia Pacific)
- Pau Tai LB-630, Modifier for PVC
- Pau Tai Unistab LCZ-108 Mixed Metal Liquid Stabilizer Calcium/Zinc for Suspension/Plastisols
- Latrobe Lescalloy® HP 9-4-30 VAC-ARC ; 13.5 in RCS Billet Size High Strength Alloy Steel
- Mitsubishi Xantar® FC 23 R Polycarbonate
- Chosun Refractories A12HM Magnesia Carbon Bricks for Electric Arc Furnace
- Fainplast Compounds FK 90 Flexible PVC, Insulation Lead Free
- Polykemi AB POLYfill PPH T8030 Polypropylene Homopolymer, Mineral Reinforced
- Fainplast Compounds PM 65/FR Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved