Lucite International Diakon® LG702 Acrylic Bead Polymer, High Transparency

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Optical Grade, Molded
Manufacturer Lucite International
Trade Name Diakon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lucite International Diakon® LG702 Acrylic Bead Polymer, High Transparency.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PMMA beads offer an exceptional transmission level of 92.5%, an increase of +0.5% in light transmission vs. granular grades - ideal for medical diagnostic devices.Information provided by Lucite International
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 0.30 %
0.30 %
ISO 62
Particle Size 600 µm
600 µm
Weight Average; Sieve Test
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Melt Flow 7.3 g/10 min
7.3 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 92
92
ISO 2039-2
Tensile Strength 80.0 MPa
11600 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Flexural Strength 110 MPa
16000 psi
ISO 178
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched (ISO) 1.80 kJ/m²
0.857 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.200 J/cm²
0.952 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 71.0 µm/m-°C
39.4 µin/in-°F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
ISO 75B
Deflection Temperature at 1.8 MPa (264 psi) 97.0 °C
207 °F
ISO 75A
Vicat Softening Point 102 °C
216 °F
ISO 306B
108 °C
226 °F
ISO 306A
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
IEC 695-2-1
Optical Properties Metric English Comments
Refractive Index 1.49
1.49
ISO 489
Haze 0.40 %
0.40 %
ASTM D1003
Transmission, Visible 92 %
92 %
ASTM D1003