- Lucite International Diakon® CRG812 Acrylic Polymer, Toughened Compound
Lucite International Diakon® CRG812 Acrylic Polymer, Toughened Compound
| Category | Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded |
| Manufacturer | Lucite International |
| Trade Name | Diakon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucite International Diakon® CRG812 Acrylic Polymer, Toughened Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Diakon® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness. The grades in the Diakon® series can be processed by injection molding or extrusion.Information provided by Lucite International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Water Absorption | 0.35 % | 0.35 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Melt Flow | 1.8 g/10 min | 1.8 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 54 | 54 | ISO 2039-2 |
| Tensile Strength | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 110 µm/m-°C | 61.1 µin/in-°F | ASTM E831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | ISO 75A |
| Vicat Softening Point | 95.0 °C | 203 °F | ISO 306B |
| 110 °C | 230 °F | ISO 306A | |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C | 1200 °F | IEC 695-2-1 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ISO 489 |
| Haze | 2.8 % | 2.8 % | ASTM D1003 |
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |