- Lucent Polymers GPCB-330 Polycarbonate+PBT, 30% Glass Fiber Reinforced, Impact Resistant
Lucent Polymers GPCB-330 Polycarbonate+PBT, 30% Glass Fiber Reinforced, Impact Resistant
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers GPCB-330 Polycarbonate+PBT, 30% Glass Fiber Reinforced, Impact Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 91.03 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | >= 3.0 % | >= 3.0 % | ASTM D638 |
| Flexural Strength | 137.93 MPa | 20005 psi | ASTM D790 |
| Flexural Modulus | 5.241 GPa | 760.2 ksi | ASTM D790 |
| Izod Impact, Notched | 1.602 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.001 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 148.89 °C | 300.00 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 740S (RL) Synthetic Oil
- Solvay Specialty Polymers Udel® P-1700 LCD Polysulfone (PSU) (Unverified Data**)
- Lehmann & Voss LUVOCOM® 50/TF/15/BK-1 Polycarbonate, with PTFE, easy flowing
- Kinlead PL11 Lamination Grade BOPP Plain Film (thickness: 12 µm)
- Kuraray HYBRAR® PS1 Thermoplastic Rubber-Polystyrene Blend
- Karina E 854-10/144-ERYM White PVC Compound
- A. Schulman POLYFORT™ FPP 2181HU High Flow, Fortified, Impact Resistant Polypropylene
- DSM Akulon® K223-HGM24 Nylon 6-30% Glass and Mineral Reinforced (European and Asian Grade) (Dry)
- Arlon 51228R025 Silicone Rubber/Fiberglass Laminate
Copyright © lookpolymers.com All Rights Reserved