Lubrizol Pellethane® 2363-80A Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | Pellethane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Pellethane® 2363-80A Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.00 - 0.0040 cm/cm | 0.00 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 23 g/10 min @Load 1.20 kg, Temperature 224 °C |
23 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 81 | 81 | ASTM D2240 |
| Tensile Strength, Ultimate | 35.8 MPa | 5190 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 50% Modulus | 0.00410 GPa | 0.595 ksi | ASTM D412 |
| 100% Modulus | 0.00610 GPa | 0.885 ksi | ASTM D412 |
| 300% Modulus | 0.0121 GPa | 1.75 ksi | ASTM D412 |
| Tear Strength | 82.3 kN/m | 470 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 25 % @Temperature 25.0 °C, Time 79200 sec |
25 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395 Method B |
| 30 % @Temperature 70.0 °C, Time 79200 sec |
30 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395 Method B | |
| Tensile Set | 30 % | 30 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature -80.0 - -30.0 °C |
94.4 µin/in-°F @Temperature -112 - -22.0 °F |
ASTM D696 |
| Vicat Softening Point | 85.0 °C | 185 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -42.0 °C | -43.6 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 210 °C | 379 - 410 °F | Molding |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- Nye Lubricants 866 (FG) Synthetic Oil
- PTS Tristar® PC-10FR-(V18) 18 MFI Flame Retardant, UV Stabilized Polycarbonate With Release
- Momentive Performance Materials Siloprenâ„¢ FFSL 7031 Fully Fluorinated Liquid Silicone Rubber
- Total EVA 1005 VN 4 Ethylene Vinyl Acetate Copolymer - Blown Film
- DuPont Performance Polymers Zytel® 80G33L NC010 Nylon 66 (Unverified Data**)
- Asahi Kasei Tenac®-C HC750 Copolymer Acetal Resin
- SABIC Innovative Plastics SABIC STAMAX 60YK270 PP
- Lucas-Milhaupt Silvaloy® 15 Brazing Alloy
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.0 PHR Thanecure® ZM
Copyright © lookpolymers.com All Rights Reserved