Lubrizol Estane® 2103-85AE Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2103-85AE Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Film and profile resinAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.00 - 0.0060 cm/cm
0.00 - 0.0060 in/in
ASTM D955
Melt Flow 24 g/10 min

@Load 8.70 kg,
Temperature 224 °C
24 g/10 min

@Load 19.2 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 88
88
ASTM D2240
Hardness, Shore D 48
48
ASTM D2240
Tensile Strength, Ultimate 32.0 MPa
4640 psi
ASTM D412
Elongation at Break 560 %
560 %
ASTM D412
50% Modulus 0.00550 GPa
0.798 ksi
ASTM D412
100% Modulus 0.00690 GPa
1.00 ksi
ASTM D412
300% Modulus 0.0121 GPa
1.75 ksi
ASTM D412
Tear Strength 82.3 kN/m
470 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 5.0
5.0
H22 Wheel, 1000g; ASTM D1044
Compression Set 25 %

@Temperature 25.0 °C,
Time 79200 sec
25 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
80 %

@Temperature 70.0 °C,
Time 79200 sec
80 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 80 %
80 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear 169 µm/m-°C

@Temperature 20.0 °C
93.9 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 67.2 °C
153 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -38.0 °C
-36.4 °F
Processing Properties Metric English Comments
Melt Temperature 182 - 199 °C
360 - 390 °F
Extrusion
188 - 204 °C
370 - 399 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 82.0 - 93.0 °C
180 - 199 °F
air dew point <-40°C