Lubrizol Estane® 2102-90A Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2102-90A Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Low compression setAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0070 cm/cm
0.0060 - 0.0070 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 1.20 kg,
Temperature 224 °C
11 g/10 min

@Load 2.65 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 94
94
ASTM D2240
Tensile Strength, Ultimate 44.8 MPa
6500 psi
ASTM D412
Elongation at Break 440 %
440 %
ASTM D412
50% Modulus 0.00840 GPa
1.22 ksi
ASTM D412
100% Modulus 0.0110 GPa
1.60 ksi
ASTM D412
300% Modulus 0.0276 GPa
4.00 ksi
ASTM D412
Flexural Modulus 0.0827 GPa
12.0 ksi
ASTM D790
Tear Strength 145 kN/m
827 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 10
10
H22 Wheel, 1000 g; ASTM D1044
Compression Set 25 %

@Temperature 25.0 °C,
Time 79200 sec
25 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
29 %

@Temperature 70.0 °C,
Time 79200 sec
29 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 30 %
30 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 150 µm/m-°C

@Temperature 20.0 °C
83.3 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 117 °C
243 °F
120°C/hr, 9.8N; ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 204 - 221 °C
399 - 430 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 88.0 - 104 °C
190 - 219 °F
air dew point <-40°C