Lubrizol Estane® 2102-80A Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2102-80A Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Low compression setAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Melt Flow 4.0 g/10 min

@Load 8.70 kg,
Temperature 190 °C
4.0 g/10 min

@Load 19.2 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 84
84
ASTM D2240
Tensile Strength, Ultimate 40.0 MPa
5800 psi
ASTM D412
Elongation at Break 575 %
575 %
ASTM D412
50% Modulus 0.00390 GPa
0.566 ksi
ASTM D412
100% Modulus 0.00550 GPa
0.798 ksi
ASTM D412
300% Modulus 0.0131 GPa
1.90 ksi
ASTM D412
Tear Strength 105 kN/m
599 pli
Die C; ASTM D624
Taber Abrasion, mg/1000 Cycles 10
10
H22 Wheel, 1000 g; ASTM D1044
Compression Set 28 %

@Temperature 25.0 °C,
Time 79200 sec
28 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
28 %

@Temperature 70.0 °C,
Time 79200 sec
28 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 50 %
50 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 158 µm/m-°C

@Temperature 20.0 °C
87.8 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 85.0 °C
185 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
Processing Properties Metric English Comments
Melt Temperature 199 - 216 °C
390 - 421 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 82.0 - 93.0 °C
180 - 199 °F
air dew pint <-40°C